| Customization: | Available |
|---|---|
| Application: | Aerospace, Architectural, Ceramic Decorations, Electronics, Industrial Ceramic, Medical, Nonferrous Alloy, Refractory, Structure Ceramic |
| Feature: | Long Time Materials |
|
Still deciding? Get samples of US$ 10/Piece
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Zhongci High Quality Zirconium Oxide 1700° C Refractory Ceramic-Material Zirconia Foam Filters for Casting Filtration
Zirconia Ceramic Foam Filter is a phosphate-free, high metling point, It is characterized by high porosity and mechanochemical stability and excellent resistance to thermal shock and corrosion from molten steel, It can effectively remove inclusions, reduce trapped gas and provide laminar flow when molten zieconia foam filtrated, it is machined to tight dimensional tolerance during production, this combination of physical properties and precise tolerance make them first choice for molten steel,alloy steel, and stainless steel, etc.
Physical and Chemical Properties
| Material | Zirconia |
| Color | Yello |
| Pore Density | 10-30ppi |
| Porosity | 80-90% |
| Refractoriness | ≤1700ºC |
| Bending Strength | >0.8Mpa |
| Compression Strength | 1.5Mpa |
| Volume-weight | 0.7-1.0 g/cm3 |
| Thermal shock resistance | 6times/1100ºC |
| Application | Steel casting & cast iron castings |
| Dimensions(mm) | Pouring rate(kg/s) | Filtration Capacity(kg) |
| 50*50*22 | 3-5 | 30 |
| 50*75*22 | 4-6 | 40 |
| 75*75*22 | 7-12 | 60 |
| 75*100*22 | 8-15 | 80 |
| 100*100*22 | 14-20 | 100 |
| Φ50*22 | 2-6 | 18 |
| Φ80*22 | 6-10 | 50 |
| Φ90*22 | 8-16 | 70 |
|
Material
|
Zirconia
|
|
Color
|
Yellow
|
|
Pore Density
|
8-60ppi
|
|
Porosity
|
80-90%
|
|
Refractoriness
|
≤1700°C
|
|
Bending Strength
|
>1.0Mpa
|
|
Compression Strength
|
>1.2Mpa
|
|
Volume-weight
|
0.9-1.5 g/cm3
|
|
Thermal shock resistance
|
6times/1100°C
|
|
Application
|
High melting point metal alloys like Steel,Alloy Steel,Stainless Steel etc
|