Lightweight Mullite Brick Insulation Fire Brick Insulating Firebrick

• Customization: Available
• Feature: Long Time Materials
• Refractoriness (℃): 1580< Refractoriness< 1770
• Shape: Brick
• Function: Thermal Insulating Brick
• Specifications: Mullite Insulation Brick
• Character: Light Weight Insulation Brick
• MOQ: 1000
• Type: Heat-Resistant Material
• Material: Alumina Block
• Transport Package: Sea-Worthy Wooden Case
• Specification: Alumina Block
• Trademark: Zhongci
• Origin: Jiangxi
• HS Code: 690220000
• Production Capacity: 500000/Month

Product Description

Product Description

 

Thermal insulation material Mullite Bricks for Heat storage

Mullite Bricks are a kind of high alumina refractory materials with mullite (3Al2O3·2SiO2) as the main crystal phase and containing 65~75% alumina content. Mullite Brick is widely used in blast furnace, hot blast stove and glass melting furnace with its various excellent properties of high temperature resistance, good thermal shock resistacne, high thermal conductivity and so on.
 

Description for Mullite Bricks

Mullite Bricks are manufacture with mullite as the main raw material through molding and firing in the high temperature. Its refractoriness is higher up to 1790ºC, its apparent initial softening temperature is 1600~1700ºC. Its cold crushing strength is 70~260MPa. It has good thermal shock resistance.

Fusion Cast Mullite Brick's Crystal is bigger than Sintered Mullite Brick's, thermal shock resistance is better than Sintered Mullite Brick's. Their high temperature properties depend on the distribution evenness of aluminium oxide content and mullite phase with glass.
 

 

There are two types of Sintered Mullite Brick and Fusion Cast Mullite Brick

• Sintered Mullite Brick is made of bauxite chamotte as the main raw material by adding little clay or raw bauxite as the binding agent through molding and firing.
• Fusion Cast Mullite Brick is produced with high bauxite, commercial alumina and fireclay as the raw materials by adding wood carbon or coke particle as the reducing agent after molding with electric melting method.

 

Corundum Mullite Brick

Corundum Mullite Brick is made of white corundum, fused mullite and sintering aids as the raw materials through homogenizing, molding and high temperature firing. Corundum Mullite Brick is widely used for all kinds of high temperature furnaces linings and thermal insulation layers with features of high temperature resistance, low thermal conductivity, high strength and high thermal shock resistance.
 

 

Application of Lightweight Mullite Brick
Lightweight Mullite Brick applies to all kinds of industry furnace hot-face lined and backing lining in metallurgical industry, petrochemical industry, building materials industry, ceramic industry, and mechanical industry. Such as cracking furnace, conversion furnace, heating equipment, refine equipment, regeneration device, hot blast stove, soaking pit furnace, heat treatment furnace, resistance furnace, tunnel kiln, roller kiln, bell kiln and glass melting furnace and etc.
Regular Specification of Lightweight Mullite Brick is 230*114*65mm
 

 

Product Parameters

 

 

Mullite Bricks Properties

• High refractoriness
• Good thermal shock resistance
• Strong acid erosion resistance
• High high-temperature strength
• Great wear resistance
• Low thermal expansion coefficient
• High thermal conductivity

Mullite Bricks Application

• Furnace roof of hot blast stove
• Furnace stack and bottom of blast furnace
• Regenerative chamber of glass melting furnace
• Ceramic high temperature furnace

Features of Lightweight Mullite Brick

1. Low thermal conductivity, low thermal capacity
2. High purity, low impurity content
3. High temperature resistance, can directly contact with fire
4. High strength, with good thermal shock resistance

Advantages of Lightweight Mullite Bricks Application In Kiln
Mullite Bricks Products have low thermal expansivity, high thermal conductivity, good thermal shock resistance, high high-temperature strength. They can resist in high temperature for long term without soften. They can resist any acid erosion, but they cannot service in the oxidizing atmosphere.
 

Mullite Bricks Manufacturers

Zhongci, as a professional Mullite Bricks Manufacturer, has always insist on manufacturing high quality Mullite Refractory Bricks such as sintered mullite bricks, fused cast mullite bricks, corundum mullite bricks, lightweight mullite bricks and etc. Contact Us for More Information!
 

Technical Data

 

Corundum Mullite Bricks

Corundum Mullite Bricks
Item/Index	Unit	HTM-1600	HTM-1750
Al2O3	%	≥85	≥90
Bulk Density	g/cm3	1.4~1.6	1.6~3.0
Cold Crushing Strength	MPa	≥15	≥20
Linear Change On Reheating 1600ºC*3h	%	≤0.2	≤0.2
Thermal Conductivity (hot-face 1000ºC)	W/m*K	≤0.6	≤1.0
Thermal Shock Resistance (air-cold 1000ºC)	Times	≥50	≥50
Maximum Service Temperature	ºC	1600	1700~1750

Sintered Mullite Brick

Sintered Mullite Brick
Item/Index	ZC-1500	ZC-1550	ZC-1600
Al2O3 %	≥70	≥80	≥85
SiO2 %	≤28	≤15	≤13
Fe2O3 %	≤0.5	≤0.5	≤0.3
Bulk Density g/cm3	1.3~1.5	1.4~1.7	1.6~1.8
Cold Crushing Strength MPa	≥8	≥8	≥10
Apparent Initial Softening Temperature ºC (0.1MPa, 0.6%)	≥1500	≥1500	≥1600
Linear Change On Reheating (1600ºC*3h)	±0.5	±0.5	±0.3
Thermal Conductivity w/(m*k) (Average temperature 800ºC)	≤0.6	≤0.7	≤0.8
Maximum Service Temperature ºC	1500	1550	1600